Material Notes:

Lexan* 3412ECR-739 Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in various opaque color options. Lexan 3412ECR-739 is a resin designed to meet the needs of high stiffness applications.

Specific Gravity 

1.30 g/cc

1.30 g/cc

ASTM D 792

Density密度

1.36 g/cc

0.0491 lb/in3

ISO 1183

Moisture Absorption at Equilibrium吸濕平衡

0.12 %

0.12 %

23°C / 50% RH; ISO 62

Water Absorption at Saturation吸水率

0.29 %
@Temperature 23.0 °C

0.29 %
@Temperature 73.4 °F

ISO 62

Linear Mold Shrinkage, Flow線性收縮率/流動

0.0020 - 0.0050 cm/cm
@Thickness 3.20 mm

0.0020 - 0.0050 in/in
@Thickness 0.126 in

SABIC Method

Linear Mold Shrinkage, Transverse 

0.0020 - 0.0050 cm/cm
@Thickness 3.20 mm

0.0020 - 0.0050 in/in
@Thickness 0.126 in

SABIC Method

Melt Flow熔體流動速率

7.0 g/10 min
@Load 1.20 kg,
Temperature 300 °C

7.0 g/10 min
@Load 2.65 lb,
Temperature 572 °F

ASTM D 1238

7.0 g/10 min
@Load 1.20 kg,
Temperature 300 °C

7.0 g/10 min
@Load 2.65 lb,
Temperature 572 °F

[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties力學性能

Metric公制數據

English英制數據

Comments測試方法

Tensile Strength at Break斷裂拉伸強度

87.0 MPa

12600 psi

Type I, 5 mm/min; ASTM D 638

90.0 MPa

13100 psi

5 mm/min; ISO 527

Tensile Strength, Yield屈服拉伸強度

90.0 MPa

13100 psi

Type I, 5 mm/min; ASTM D 638

95.0 MPa

13800 psi

5 mm/min; ISO 527

Elongation at Break斷裂伸長率

3.2 %

3.2 %

5 mm/min; ISO 527

Elongation at Yield屈服伸長率

2.8 %

2.8 %

5 mm/min; ISO 527

3.1 %

3.1 %

Type I, 5 mm/min; ASTM D 638

Tensile Modulus拉伸模量

5.50 GPa

798 ksi

5 mm/min; ASTM D 638

6.00 GPa

870 ksi

1 mm/min; ISO 527

Flexural Yield Strength彎曲屈服強度

140 MPa

20300 psi

2 mm/min; ISO 178

156 MPa

22600 psi

1.3 mm/min, 50 mm span; ASTM D 790

Flexural Modulus彎曲彈性模量

5.00 GPa

725 ksi

1.3 mm/min, 50 mm span; ASTM D 790

5.50 GPa

798 ksi

2 mm/min; ISO 178

Izod Impact, Notched懸臂梁缺口沖擊強度  

1.07 J/cm
@Temperature -30.0 °C

2.00 ft-lb/in
@Temperature -22.0 °F

ASTM D 256

1.10 J/cm
@Temperature 23.0 °C

2.06 ft-lb/in
@Temperature 73.4 °F

ASTM D 256

Izod Impact, Notched懸臂梁缺口沖擊強度(ISO)  

6.00 kJ/m2
@Temperature -30.0 °C

2.86 ft-lb/in2
@Temperature -22.0 °F

80*10*3; ISO 180/1A

7.00 kJ/m2
@Temperature 23.0 °C

3.33 ft-lb/in2
@Temperature 73.4 °F

80*10*3; ISO 180/1A

Izod Impact, Unnotched懸臂梁無缺口沖擊強度 (ISO)

35.0 kJ/m2
@Temperature 23.0 °C

16.7 ft-lb/in2
@Temperature 73.4 °F

80*10*3; ISO 180/1U

35.0 kJ/m2
@Temperature -30.0 °C

16.7 ft-lb/in2
@Temperature -22.0 °F

80*10*3; ISO 180/1U

Charpy Impact Unnotched夏比缺口試樣沖擊

4.00 J/cm2
@Temperature 23.0 °C

19.0 ft-lb/in2
@Temperature 73.4 °F

Edgew 80*10*3 sp=62mm; ISO 179/1eU

4.00 J/cm2
@Temperature -30.0 °C

19.0 ft-lb/in2
@Temperature -22.0 °F

Edgew 80*10*3 sp=62mm; ISO 179/1eU

Charpy Impact, Notched夏比缺口沖擊

0.500 J/cm2
@Temperature -30.0 °C

2.38 ft-lb/in2
@Temperature -22.0 °F

V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA

0.600 J/cm2
@Temperature 23.0 °C

2.86 ft-lb/in2
@Temperature 73.4 °F

V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA

Impact Test沖擊試驗數據

20.0 J
@Temperature 23.0 °C

14.8 ft-lb
@Temperature 73.4 °F

Instrumented Impact Total Energy; ASTM D 3763

Electrical Properties電性能

Metric公制數據

English英制數據

Comments測試方法

Volume Resistivity體積電阻率

>= 1.00e+15 ohm-cm

>= 1.00e+15 ohm-cm

IEC 60093

Surface Resistance表面電阻

>= 1.00e+15 ohm

>= 1.00e+15 ohm

ROA; IEC 60093

Dielectric Constant介電常數  

3.3
@Frequency 1.00e+6 Hz

3.3
@Frequency 1.00e+6 Hz

IEC 60250

3.3
@Frequency 50.0 - 60.0 Hz

3.3
@Frequency 50.0 - 60.0 Hz

IEC 60250

Dissipation Factor耗散因數

0.010
@Frequency 1.00e+6 Hz

0.010
@Frequency 1.00e+6 Hz

IEC 60250

0.020
@Frequency 50.0 - 60.0 Hz

0.020
@Frequency 50.0 - 60.0 Hz

IEC 60250

Arc Resistance電弧電阻

0.00 - 60 sec

0.00 - 60 sec

Tungsten, PLC code 7; ASTM D 495

Comparative Tracking Index跟蹤指數

175 - 250 V

175 - 250 V

PLC code 3; UL 746A

Hot Wire Ignition, HWI 熱線圈點燃測試

>= 120 sec

>= 120 sec

PLC code 0; UL 746A

High Amp Arc Ignition, HAI高電流電弧點燃測試

15 - 30 arcs

15 - 30 arcs

surface, PLC code 3; UL 746A

High Voltage Arc-Tracking Rate, HVTR高壓電弧跟蹤速度

80.0 - 150 mm/min

3.15 - 5.91 in/min

PLC code 3; UL 746A

Thermal Properties熱性能

Metric公制數據

English英制數據

Comments測試方法

CTE, linear, Parallel to Flow線性熱膨脹系數  

30.0 μm/m-°C
@Temperature -40.0 - 40.0 °C

16.7 μin/in-°F
@Temperature -40.0 - 104 °F

ASTM E 831

30.0 μm/m-°C
@Temperature 23.0 - 80.0 °C

16.7 μin/in-°F
@Temperature 73.4 - 176 °F

ISO 11359-2

CTE, linear, Transverse to Flow 線性熱膨脹系數/橫向

70.0 μm/m-°C
@Temperature -40.0 - 40.0 °C

38.9 μin/in-°F
@Temperature -40.0 - 104 °F

ASTM E 831

70.0 μm/m-°C
@Temperature 23.0 - 80.0 °C

38.9 μin/in-°F
@Temperature 73.4 - 176 °F

ISO 11359-2

Deflection Temperature at熱變形溫度0.46 MPa (66 psi) 

141 °C

286 °F

Flatw 80*10*4 sp=64mm; ISO 75/Bf

Deflection Temperature at熱變形溫度1.8 MPa (264 psi) 

136 °C

277 °F

Flatw 80*10*4 sp=64mm; ISO 75/Af

141 °C
@Thickness 3.20 mm

286 °F
@Thickness 0.126 in

unannealed; ASTM D 648

Vicat Softening Point維卡軟化點

145 °C

293 °F

Rate B/50; ISO 306

146 °C

295 °F

Rate B/120; ISO 306

147 °C

297 °F

Rate B/50; ASTM D 1525

UL RTI, Electrical相對溫度指數

130 °C

266 °F

UL 746B

UL RTI, Mechanical with Impact機械沖擊熱指數

130 °C

266 °F

UL 746B

UL RTI, Mechanical without Impact無機械沖擊熱指數

130 °C

266 °F

UL 746B

Flammability, UL94阻燃等級  

V-0
@Thickness 1.50 mm

V-0
@Thickness 0.0591 in

UL 94

5VA
@Thickness 3.00 mm

5VA
@Thickness 0.118 in

UL 94

Oxygen Index氧指數

40 %

40 %

LOI; ISO 4589

Glow Wire Test灼熱絲測試  

825 °C
@Thickness 1.00 mm

1520 °F
@Thickness 0.0394 in

Glow Wire Ignitability Temperature; IEC 60695-2-13

960 °C
@Thickness 1.00 mm

1760 °F
@Thickness 0.0394 in

Glow Wire Flammability Index; IEC 60695-2-12